Scope

The

purpose of this test method is to provide a

procedure for examining glass fabric to determine its con-

struction, including its weight, thickness, strength, and type of

weave. Since this method may be used to examine glass fab-

ric used in PCB laminate and pre-impregnated ‘‘B’’ stage

glass fabric, the method provides a procedure for removing

any obscuring resin by a combustion process.

Applicable Documents

IPC-EG-140

Specification

for Finished Fabric Woven from

‘‘E’’ Glass for Printed Boards

Test Specimen

3.1

Three

pieces of material, 5 cmx5cm

Equipment/Apparatus

4.1

Muffle

furnace capable of maintaining 538°C ± 14°C

4.2 Analytical

balance capable of weighing to the nearest

milligram (0.001 g)

4.3 Micrometer

capable of measuring to the nearest 0.0025

4.4

Binocular

microscope, magnification to 30X

Procedure

5.1

minimum of three specimens of each test material

shall be tested by the following procedure: Place a specimen

in a crucible of suitable size and place in muffle furnace main-

tained at 538°C ± 14°C for 30 minutes. Remove from muffle

furnace and allow to cool.

5.2

Examine Residual Material

5.2.1

the residue shows any evidence of glass fusion,

repeat 5.1, but with the muffle furnace temperature main-

tained at 488°C ± 14°C. If there is evidence of glass fusion at

this lower temperature, again repeat the procedure of 5.1,

lowering the temperature in 50°C increments until there is no

evidence of glass fusion.

5.2.2

the residue shows evidence of incomplete removal

of resin, increase the temperature of the furnace by 50°C and

repeat 5.1.

5.2.3

After

the initial period and cooling to room tempera-

ture, the residual glass fabric must be white, free of resin resi-

due, and exhibit no evidence of glass fusion.

5.3

Thickness Measurement

Place

the glass fabric speci-

men between two flat plates and measure the thickness with

a micrometer. Remove the glass fabric specimen and mea-

sure the thickness of the two flat plates. The thickness of the

glass fabric shall be determined by subtracting the thickness

of the two flat plates without the glass fabric from the mea-

surement obtained with the glass fabric between the plates.

The thickness of at least three specimens shall be measured

and recorded. The thickness of each specimen shall be deter-

mined as the average of five separate measurements.

5.4

Glass Fabric Weight

5.4.1

The

length and width dimensions of the glass fabric

specimens shall be measured to the nearest 0.25 mm.

5.4.2

The

weight of the specimen shall be determined using

the analytical balance and weighing to the nearest milligram.

5.4.3

The

weight of the glass fabric shall be determined

using IPC-EG-140.

5.5

Fabric Construction

The

number of yarns in the warp

and fill used in constructing the fabric shall be determined by

counting a 2.5 sq. cm area of the fabric using a microscope.

5.6 All

other properties in Table 1 shall be as specified in the

procurement document.

5.7

Report

The

results of testing glass fabric by this test

method shall be reported in a written report, which (as a mini-

mum) contains the following:

1. Certification that the test was performed in accordance

with this test method

2. Identification of the specimens tested

3. Dimensions of each specimen (length and width)

The

Institute for Interconnecting and Packaging Electronic Circuits

2215 Sanders Road • Northbrook, IL 60062-6135

IPC-TM-650

TEST

METHODS MANUAL

Number

2.3.11

Subject

Glass

Fabric Construction

Date

4/73

Revision

Originating Task Group

N/A

Material

in this Test Methods Manual was voluntarily established by Technical Committees of the IPC. This material is advisory only

and its use or adaptation is entirely voluntary. IPC disclaims all liability of any kind as to the use, application, or adaptation of this

material. Users are also wholly responsible for protecting themselves against all claims or liabilities for patent infringement.

Equipment referenced is for the convenience of the user and does not imply endorsement by the IPC.

age1of3

电子技术应用　　　　　　　ｗｗｗ．ＣｈｉｎａＡＥＴ．ｃｏｍ

Thickness of the specimens

5. Fabric construction

6. Weight of each specimen in ounces per square yard

7. Results of any additional tests required by the test request

or purchase document

8. Conclusions as to whether the test specimens meet the

requirements of the glass fabric specified

IPC-TM-650

Number

2.3.11

Subject

Glass

Fabric Construction

Date

4/73

Revision

age2of3

电子技术应用　　　　　　　ｗｗｗ．ＣｈｉｎａＡＥＴ．ｃｏｍ

able 1

Cloth

No.

Nominal

idth

Inches

Thickness

Inch

Weight

Per

Square

Yard

Ounces

Yarn,

Warp,

and Fill Construction

Minimum

Breaking

Strength Per

Inch of Width

Yards per

Standard

Roll Type of Weave

Warp

Pounds

Fill

Pounds

106

38 0.0015 0.85 900-1/0 56x56 46 52 250 ± 25 Plain

108 38 0.0020 1.43 900-1/2 60x47 70 40 250 ± 25 Plain

112 38 0.0030 2.09 450-1/2 40x39 82 80 250 ± 25 Plain

113 38 0.0030 2.46 450-1/2

900-1/2

60x64 123 60 250 ± 25 Plain

116 38 0.0040 3.16 450-1/2 60x58 123 120 250 ± 25 Plain

119 38 0.0040 2.80 450-1/2 54x50 110 100 250 ± 25 Plain

120 38 0.0040 3.16 450-1/2 60x58 125 120 250 ± 25 4-harness satin

126-150 38 0.0060 5.50 150-1/2 34x32 225 195 250 ± 25 Plain

126 38 0.0065 5.37 450-3/2 34x32 205 185 250 ± 25 Plain

127 38 0.0070 6.00 450-3/2 42x32 225 185 250 ± 25 Plain

128 38 0.0070 6.00 225-1/3 42x32 250 200 250 ± 25 Plain

128-150 38 0.0067 6.00 150-1/2 42x32 250 200 250 ± 25 Plain

140 38 0.0100 8.70 450-4/3 32x21 400 290 125 ± 25 Plain

141 38 0.0100 8.70 225-2/3 32x21 400 290 125 ± 25 Plain

143 38 0.0090 8.90 225-3/2

450-1/2

49x30 611 56 125 ± 25 4-harness satin

143-150 38 0.0086 9.40 150-2/2

450-1/2

49x30 660 70 125 ± 25 4-harness satin

148 38 0.0120 10.10 450-3/5 30x19 450 360 125 ± 25 Plain

149 38 0.0120 10.80 225-2/4 30x19 450 360 125 ± 25 Plain

161 38 0.0150 12.20 450-4/5 28x16 550 450 125 ± 25 Plain

162 38 0.0150 12.20 225-2/5 28x16 450 350 125 ± 25 Plain

164 38 0.0150 12.60 225-4/3 20x18 500 450 125 ± 25 Plain

164-150 38 0.0140 13.00 150-4/2 20x18 500 450 125 ± 25 Plain

181 38 0.0085 8.90 225-1/3 57x54 340 330 125 ± 25 8-harness satin

181-150 38 0.0080 9.50 150-1/2 56x54 350 325 125 ± 25 Plain

182 38 0.0130 12.40 225-2/2 60x56 440 400 125 ± 25 8-harness satin

182-150 38 0.0134 12.65 150-1/3 60x56 440 400 125 ± 25 Plain

183 38 0.0180 16.75 225-3/2 54x48 650 620 75 ± 15 8-harness satin

184 38 0.0270 25.90 225-4/3 42x36 950 800 50 ± 10 8-harness satin

184-150 38 0.0246 24.16 150-4/2 44x35 950 800 50 ± 10

573-150 38 0.0110 8.00 150-3/2 16x16 335 316 125 ± 25 Plain

1000-150 38

and

0.0130 9.66 150-4/2 16x14 450 410 125 ± 25 Plain

1044-150 38 0.0220 19.20 ...... 16x14 450 410 125 ± 25 Plain

1523-150 38 0.0140 11.70 150-3/2 28x20 525 400 125 ± 25 Plain

1527-150 38 0.0150 12.90 150-3/3 17x17 535 485 125 ± 25 Plain

IPC-TM-650

Number

2.3.11

Subject

Glass

Fabric Construction

Date

4/73

Revision

age3of3