SEMI M3-0304 © SEMI 1978, 2004 6 Table 1 Dimensiona l Specification for Sapphire Substrates Nominal Diameter 2 inch 3 inch 100 mm 125 mm 150 mm Previous Standard SEMI M3.2-91 SEMI M3.4-91 SEMI M3.5-92 SEMI M3.7-91 SEMI M…

100%1 / 7923
SEMI M3-0304 © SEMI 1978, 2004 5
Figure 2
Sapphire Surface Orientation
Figure 3
Primary and Secondary Flat Locations
Figure 4
Measurement Points for Determination of Layer Thickness Variation
SEMI M3-0304 © SEMI 1978, 2004 6
Table 1 Dimensional Specification for Sapphire Substrates
Nominal Diameter 2 inch 3 inch 100 mm 125 mm 150 mm
Previous Standard SEMI M3.2-91 SEMI M3.4-91 SEMI M3.5-92 SEMI M3.7-91 SEMI M3.8-91
Property Units Min Max Min Max Min Max Min Max Min Max
DIAMETER mm
in.
50.55
1.990
51.05
2.010
76.95
2.990
76.45
3.010
99.0
3.90
101.0
3.97
124.0 126.0 149.0 151.0
THICKNESS,
CENTER POINT
µ m
in.
280
0.011
380
0.015
380
0.15
480
0.19
500
0.0197
550
0.0216
600 650 650 700
PRIMARY FLAT
LENGTH
mm
in.
14.23
0.56
17.52
0.69
19
0.75
25
1.00
30.0
1.182
35.0
1.377
40.0 45.0 55.0 60.0
SECONDARY FLAT
LENGTH
mm.
in.
6.35
0.25
9.65
0.38
9.6
0.38
12.7
0.50
16.0
0.630
20
0.787
18.0 22.0 35.0 40.0
BOW, max µ m
in.
38
0.0015
51
0.002
40 60 60
WARP, max µ m
in.
Not Specified Not Specified
40 60 60
TOTAL THICKNESS
VARIATION, max
µ m
in.
51
0.002
76
0.0030
56
0.0019
50 60
SURFACE
ORIENTATION
}0211{
± 2.0° (NOTE 3)
NOTES 1 1 2 2 2
NOTE 1: For referee purposes, the U.S. Customary units apply. Conversion to metric (SI) equivalents was done following the maximum-
minimum convention in which the minimum values are rounded up and the maximum values are rounded down to ensure that the equivalent
range is always inside the referee range. If the metric equivalents are used for incoming inspection measurements, the rightmost digit of
minimum values should be reduced by 1 and the rightmost digit of maximum values should be increased by 1 to avoid rejection of material that is
within the specification when measured by the referee system of units. CAUTION — The significance of the rightmost digit may vary,
depending on the quantity being measured and the precision of the test procedure. Refer to the relevant test method for precision data that can be
used to construct appropriate guard bands.
NOTE 2: For referee purposes, the metric (SI) units apply. Conversion to U.S. Customary equivalents was done following the maximum-
minimum convention in which the minimum values are rounded up and the maximum values are rounded down to ensure that the equivalent
range is always inside the referee range. If the metric equivalents are used for incoming inspection measurements, the rightmost digit of
minimum values should be reduced by 1 and the rightmost digit of maximum values should be increased by 1 to avoid rejection of material that is
within the specification when measured by the referee system of units. CAUTION — The significance of the rightmost digit may vary,
depending on the quantity being measured and the precision of the test procedure. Refer to the relevant test method for precision data that can be
used to construct appropriate guard bands.
NOTE 3: Equivalent
}0211{ r planes are ),0121(and),2101(),0211( see Figure 1.
Table 2 Flatness Classes for Sapphire Substrates
Class Flatness (TIR), µm
I 25 max
II 14 max
III 10 max
IV 8 max
V 6 max
SEMI M3-0304 © SEMI 1978, 2004 7
APPENDIX 1
SPECIFICATION FOR 3 INCH RECLAIMED SAPPHIRE SUBSTRATES
NOTICE: The material in this appendix is an official part of SEMI M3 and was approved by full letter ballot
procedures on September 3, 2003. The material in this appendix was originally included in SEMI M3.6-88,
Standard for 3 inch Reclaimed Sapphire Substrates.
A1-1.1 Dimensional specifications for 3 inch reclaimed sapphire substrates are given in Table A1-1.
A1-1.2 Surface orientation shall be as received for reclamation.
A1-1.3 Flat location(s) shall be as received for reclamation.
A1-1.4 Flatness shall be classified in accordance with Table 2. The amount of surface damage and flatness of the
as-received substrate determines final flatness.
A1-1.5 Front surface finish shall be in accordance with the purchase order or contract. See Related Information 2
for recommendations on acceptable front surface finish level.
A1-1.6 Back surface finish shall be as received for reclamation.
A1-1.7 Other characteristics, including sampling, test methods, surface defect limits, certification, and packing and
marking, shall be as specified in SEMI M3.
Table A1-1 Dimensional Specification
Property Min Max Units (see NOTE 1)
DIAMETER As received for reclamation.
THICKNESS, CENTER POINT
(see NOTE 2)
0.014
360
0.019
480
in.
µm
FLAT LENGTH As received for reclamation.
BOW, max 0.002
51
in.
µm
NOTE 1: For referee purposes, the U.S. Customary units apply. Conversion to metric (SI) equivalents was done following the maximum-
minimum convention in which the minimum values are rounded up and the maximum values are rounded down to ensure that the equivalent
range is always inside the referee range. If the metric equivalents are used for incoming inspection measurements, the rightmost digit of
minimum values should be reduced by 1 and the rightmost digit of maximum values should be increased by 1 to avoid rejection of material that is
within the specification when measured by the referee system of units. CAUTION — The significance of the rightmost digit may vary,
depending on the quantity being measured and the precision of the test procedure. Refer to the relevant test method for precision data that can be
used to construct appropriate guard bands.
NOTE 2: Amount of surface damage and flatness of as-received substrate determines final substrate thickness.